Method and test kit for determining hydroxy aromatic compounds

ABSTRACT

A method and test kit for the detection of hydroxy substituted aromatic compounds using a titanium film (12, 23) which reacts with the compound to change the light absorbance. Preferred films are prepared by reaction of a titanium alkoxide with an aliphatic carboxylic acid. The change in light absorbance of the film is preferably detected with an ultraviolet-visible spectrophotometer. Preferably the film is provided on a transparent slide (22) or on an inside wall of a spectrophotometer cell (10). The cells (10 and 20) are provided with covers (13 and 14) for holding the solution to allow the hydroxy substituted compounds to react with the film.

This application is a continuation of application Ser. No. 08/373,603 filed on Jan. 17, 1995 now abandoned, which is a division of application Ser. No. 08/301,652, filed Sep. 6, 1994, now U.S. Pat. No. 5,462,878.

BACKGROUND OF THE INVENTION

(1) Field of the Invention

The present invention relates to a method and test kit for determining the presence of a hydroxy substituted aromatic compound in a solution using titanium films which change light absorbance in the presence of the compound. In particular, the present invention relates to the use of preferred films prepared from a titanium alkoxide and an aliphatic carboxylic acid.

(2) Prior Art

The polymerization of titanium alkoxide results from the hydrolysis of alkoxide groups as shown in equation (1).

    M--OR+H.sub.2 O→M--OH+ROH                           (1)

Propagation occurs by subsequent polycondensation reactions. Two competitive mechanisms are possible during the polycondensation; they are olation and oxolation reactions. Olation is the formation of hydroxy bridges through the elimination of solvent molecules,

    M--OH+MOHX→M--OH--M+XOH                             (2)

(X═H or alkyl group)

and, oxolation is the formation of oxygen bridges through the elimination of H₂ O or ROH,

    M--OH+MOX→M--O--M+XOH                               (3)

(X═H or alkyl group)

These reactions result in the transformation of the titanium alkoxide into the titanium oxide network. The contribution of each reaction determines the structure and morphology of the titanium oxide network.

The reaction of carboxylic acid with titanium alkoxide has been used to prepare titanium alkoxide precursors (Sanchez, C., et al., J. Non-Cryst. Solids 100, 65 (1988); Sanchez, C., et al., New J. Chem. 14, 513 (1990); and Sanchez, C., et al., in "Ultrastructure Processing of Advance Ceramics", Mackenzie, J. D.,; Ulrich, D. R. Eds, Wiley, New York P. 77 (1988)). Changes in the titanium alkoxide precursors modify the hydrolysis and polycondensation reactions of the titanium alkoxide (Doeuff, S., et al., J. Non-Cryst. Solids 89, 206 (1987)). There are several U.S. patents on the preparation of polymeric titanium complexes with carboxylic acids (U.S. Pat. No. 2,621, 193 (Dec. 9, 1952) to Langkammerer; U.S. Pat. No. 2,621,194 (Dec. 9, 1952; and U.S. Pat. No. 2,621,195 (Dec. 9, 1952) to Haslam). Titanium oxide gels (Gagliardi, C. D., et al., Mat. Res. Soc. Symp. Proc., 155, 127 (1989); and Livage, J., Mat. Res. Soc. Symp. Proc. 73, 717 (1986)) and films (Gagliardi, C. D., et al., Mat. Res. Soc. Symp. Proc., 180, 801 (1990)) have also been prepared by the controlled hydrolysis of the titanium alkoxide carboxylic acid precursors. The actual titanium oxide network has not been fully characterized. It is possible that the titanium oxide network may still undergo further reactions.

Color development is observed with titanium phenoxy complexes. For example dichlorodiphenoxy-titanium (IV) (Watenpaugh, K., et al., Inorg. Chem. 5, 1782 (1966)) is red, tetraphenoxytitanium (IV) monophenolate ((a) Svetich, G. W., et al., J. Am. Chem. Soc. Chem. Commun., 676 (1971); (b) Svetich, G. W., et al., Acata Cryst. B28, 1760 (1972); and (c) Malhotra, K. C., et al., J. Organomet. Chem., 239, 159 (1982)) is an orange-red, isoproyltriphenoxy-titanium (IV) is a bright yellow (Varma, I. D., et al., J. Indian, Chem. Soc., 38, 147 (1961)), and NH₄ !₂ Ti (catecholate)₃)!.2H₂ O¹⁴ is a rust color. U.S. Pat. No. 4,043,820 to Landau discloses using titanium-catechol chelate to develop color when applied as an ink to alkaline paper (U.S. Pat. No. 4,043,820 (Aug. 23, 1977) to Landau). Such complexations are well established in the liquid phase where coordination sites to the titanium IV are easily accessible but no such chelation has been reported when TI(IV) ions are immobilized in a solid network.

There is a need for a simple, reliable method for the detection of phenolic compounds, particularly in the field when testing water sources for the presence of such contaminants. The prior art has used sophisticated instrumentation such as gas chromatograph or mass spectrograph for this purpose; however, the use of such instrumentation in the field produces unreliable results and is expensive.

OBJECTS

It is therefore an object of the present invention to provide a reliable and inexpensive method for the detection of hydroxy substituted aromatic compounds. Further, it is an object of the present invention to provide a method which can be easily adapted for use in the field. These and other objects will become increasingly apparent by those skilled in the art from the following description and the drawings.

IN THE DRAWINGS

FIG. 1 is a graph showing a titanium film prepared as in Example 4 with the concentration as a function of absorbance for phenol solutions.

FIG. 2 is a graph showing a titanium film prepared as in Example 4 with the concentration as a function of absorbance for a pyrocatechol (1,2-dihydroxybenzene) solution.

FIG. 3 is a front cross-sectional view showing a spectrophotometer cell 10 having a titanium film 12 deposited inside.

FIG. 3A is a cross-sectional view of FIG. 3 along line 3A--3A.

FIG. 4 is a front cross-sectional view of a spectrophotometer cell 20 showing a slide 22 with a titanium film 23 deposited thereon.

FIG. 4A is a cross-sectional view along line 4A-4A of FIG. 4.

GENERAL DESCRIPTION

The present invention relates to a method for determining the presence of a hydroxy substituted aromatic compound in a solution which comprises: providing a titanium film which changes light absorbance in the presence of the hydroxy substituted aromatic compound in solution; and contacting the film with the solution so as to determine the presence of the hydroxyaromatic compound because of a change of light absorbance of the film when the solution contains the hydroxy substituted aromatic compound.

The present invention also relates to a test kit for determining the presence of a hydroxy substituted aromatic compound in solution which comprises: a titanium film deposited on a transparent element which can be inserted in a spectrophotometer after contact with the solution. Preferably the transparent element is a sealable container which is openable for inserting the solution and, wherein the container is free of the aromatic compound.

The preferred titanium films are formed from the reaction of a titanium alkoxide and an aliphatic carboxylic acid. The alkoxide preferably contains 3 to 32 carbon atoms and the aliphatic carboxylic acid preferably contains between about 2 and 22 carbon atoms. The most preferred titanium alkoxide is titanium isopropoxide. The most preferred aliphatic carboxylic acids are valeric and lauric acids, alone or together. Usually the reaction is conducted in an aqueous solution.

Various hydroxy substituted aromatic compounds can be detected by the method and test kit of the present invention. Phenolic compounds like phenol, are readily detected. Other compounds which are detected are shown in the Examples.

Some compounds are not detected and it is believed that size and/or blocked or hindered hydroxy groups may be the reason for non-detection because the compounds do not react with the titanium film. Another possibility may be the development of complexes absorbing deeper into the ultraviolet region, therefore being undetectable to the eye and masked by the film absorption cutoff. The results are quantitative and reproducible.

Usually the detection is in a suspect aqueous solution since these are encountered in the field. The suspect aqueous solutions are tested using a spectrophotometer, preferably one operating in the visible to ultraviolet (UV) range. Such instruments are well known to those skilled in the art and can operate on the typical 12 volt system found in vehicles used in the field. If necessary an auxiliary generator can be used if a higher voltage is necessary. Hand-held, battery operated spectrophotometers are also suitable.

As shown in FIGS. 3 and 3A the transparent element can be a spectrophotometer cell 10 coated with the film 12. The cell 10 has a container portion 11 and a cover 13. The cell 10 can be disposed of or recycled by removing the old film 12 and depositing a new film. Silica glass can be used to make the cell 10. As shown in FIGS. 4 and 4A, a cell 20 can also be used with a container portion 21 and cover 24 and a slide 22 coated with the titanium film 23. The slide 22 is of the type used with optical microscopes.

SPECIFIC DESCRIPTION

In the examples below, the titanium films change from a colorless transparent film to a yellow or orange color depending on the type and the concentration of a phenolic compound (hydroxybenzene compound) present in aqueous solutions brought in contact with the film. This is because of the change in absorbance of the film in the presence of the phenolic compound. When these titanium films are soaked in 100 ppm aqueous pyrocatechol (1,2-dihydroxybenzene) solutions the titanium films turn to an orange color.

(1) Preparation of the Titanium Films

In the examples that follow the titanium alkoxide carboxylate films produced are referred to as "titanium films".

EXAMPLE 1

Titanium film I: Valeric acid (1.6 ml, 1.52×10⁻² moles) was added to titanium isopropoxide (0.50 ml, 1.63×10⁻³ moles) the solution was mixed, water (42 L, 2.33×10⁻³ mole) was added, and the solution was stirred again.

EXAMPLE 2

Titanium film II: Valeric acid (2.7 ml, 2.48 ×10⁻² moles) was added to titanium isopropoxide (1.00 ml, 3.26×10⁻³ moles) the solution was mixed, water (0.61 mL, 3.39×10⁻² mole) was added, and the solution was stirred again.

EXAMPLE 3

Titanium film III: Valeric acid (1.6 ml, 1.52×10⁻² moles) was added to titanium isopropoxide (0.5 ml, 1.63×10⁻² moles) the solution was mixed, and then water (0.30 mL, 1.67×10⁻² mole) was added, and the solution was stirred again.

EXAMPLE 4

Titanium film IV: Lauric acid (0.250 gm, 1.25×10⁻³ mole) was added to titanium isopropoxide (1.00 ml, 3.26×10⁻³ mole). The mixture was heated with a hot air gun until all of the lauric acid dissolved. Valeric acid (2.50 ml, 2.30×10⁻² moles) was added to the hot solution. The solution was stirred and an exothermic reaction took place. Water (92 μL, 5.11×10⁻³ mole) was then added, and the solution was stirred.

EXAMPLE 5

Titanium film V: Lauric acid (0.250 gm, 1.25×10⁻³ mole) was added to titanium isopropoxide (1.00 ml, 3.26×10⁻³ mole). The mixture was healed with a hot air gun until all of the lauric acid dissolved. Valeric acid (2.50 ml, 2.30×10⁻² moles) was added to the hot solution. The solution was stirred and an exothermic reaction took place. Water (0.61 ml, 3.39×10⁻² mole) was then added, and the solution was stirred.

EXAMPLE 6

Titanium film VI: Lauric acid (0.250 gm, 1.25×10⁻³ mole) was added to titanium isoproproxide (1.00 ml, 3.26×10⁻³ mole). The lauric acid was dissolved by placing the mixture in a sonic bath for 2 minutes. Valeric acid (2.50 ml, 2.30×10⁻² moles) was added and the solution was stirred. Water (0.61 mL, 3.39×10⁻² mole) was then added, and the solution was stirred.

EXAMPLE 7

Titanium film VII: Lauric acid (0.250 gm, 1.25×10⁻³ mole) was added to titanium isopropoxide (1.00 ml, 3.26×10⁻³ mole). The mixture was heated with a hot air gun until all of the lauric acid dissolved. Valeric acid (2.50 ml, 2.30×10⁻² moles) was added to the hot solution. The solution was stirred and an exothermic reaction took place. TMOS (tetramethyl ortho silicon, 1.0 mL, 6.65×10⁻⁴ moles) was added and stirred into the reaction mixture. Water (0.61 mL, 3.39×10⁻² mole) was then added and the reaction mixture was stirred.

EXAMPLE 8

Titanium film VIII: Lauric acid (0.250 gm, 1.25×10⁻³ mole) was added to titanium isopropoxide (1.00 ml, 3.26×10⁻³ mole). The mixture was heated with a hot air gun until all of the lauric acid dissolved. Valeric acid (2.50 ml, 2.30×10⁻² moles) was added to the hot solution. The solution was stirred and an exothermic reaction took place. Dow Corning Z-6020 (N-(β-aminoethyl)-γ-aminopropyltrimethysilane) (0.3 mL, 1.38×10⁻³ moles) was added and stirred into the reaction mixture. Water (0.61 mL, 3.39×10⁻² moles) was then added and the reaction mixture was stirred.

(2) Film Formation and Instrumentation

The titanium films were prepared from the polymers of Examples 1 to 8 by spin casting 60 μL of the film solution on a 50 mm×8 mm silica slide. The titanium film is placed in a quartz cell, and the film was first soaked in water, for 10 minutes, then the water was removed and the phenolic solution was placed in the cell. A Perkin-Elmer Lambda 3A UV/Vis Spectrophotometer was used to record the electronic absorption spectra.

(a) When the titanium film I was soaked in water the film turned to a very light yellow. If the film was exposed to air for several days the titanium film also turned to a very light yellow. The titanium film was soaked for 2 hours in 112 ppm catechol and the absorbance maximum was 0.178 at 350 nm (the titanium film was 6 days old).

(b) When the titanium film II was soaked in water the film turned to a very light yellow. If the film is exposed to air for several days the titanium film also turns to a very light yellow. The titanium film was soaked in 112 ppm catechol for 2 hours and the absorbance maximum was 0.260 at 350 nm.

(c) When the titanium film IV was soaked in water a very light yellow color in the titanium film was noticed if the film was placed next to a titanium film made from Example II. The titanium film IV was soaked in 105 ppm catechol for two hours and the absorption maximum was 0.315 at 350 nm.

The following compounds result in color changes when contacted with the titanium film IV. Phenol, 1-naphthol, 3,5-dihydroxybenzoic acid, catechol (1,2-dihydroxybenzene), resorcinol (1,3-dihydroxybenzene), pyrogallol (1,2,3-trihydroxybenzene), phloroglucinol (1,3,5-trihydroxybenzene), anisole. Others that react are orcinol, chrysin, esculetin 7-hydroxy-4-methyl coumarin. Phenolic complexes that have two hydroxyl groups in the 1,2 position (catechol, and pyrogallol) appeared to interact more readily with the titanium film, and yield more intense absorbance bands. For similar concentrations of catechol and pyrogallol, soaking the titanium films the same amount of time resulted in similar intensities of the absorption. The intensity of catechol and pyrogallol absorption bands were approximately 8 times greater than that of phenol, resorcinol, hydroquinone, and phloroglucinol absorptions. The lowest detection of catechol was 305 ppb (2.77×10⁻⁴ M), and for phenol it was 32.6 ppm (3.46 ×10⁻ M).

The following is a list of compounds that do not result in color changes when contacted with the titanium film IV: aniline, benzaldehyde, benzene, unsaturated alcohols, disodium L-tyrosine, benzyl alcohol, 4-amino-3,5,6-trichloropicolinic sodium salt, pyranine, heptafluorobutyric acid, aluminum nitrate, BHT, 4,5-dihydroxynaphthalene-2,7-disulfonic acid (disodium salt) Acac, EDTA, 1,10-phenanthroline, 2,5-dichloro 3,6-dihydroxyl-p-benzoquinone (chloranilic acid), tetrachloro-1,2-benzoquinone (o-chloronil) juglone, lawsone, veratrole, sorbitol, dopamine, 1,2-naphthoquinone, phloretin. 1,2,4-Trihydroxybenzene dissolved in water produced a pink solution, and the titanium film turned pink.

(e) When the titanium film V was soaked in water there was no color change in the film. The titanium film was soaked in 116 ppm catechol for 2 hours the absorbance maximum was 0.313 at 350 nm.

(f) When the titanium film VI was soaked in water there was no color change in the film. The titanium film was soaked in 116 ppm catechol for 2 hours the absorbance maximum was 0.360 at 350 nm.

(g) The mixed titanium silicon film was placed in a catechol solution and the film turned yellow-brown.

(h) The mixed titanium silicon film VIII film was stable in water, but turns cloudy white when placed in methanol.

It is intended that the foregoing description and Examples be only illustrative of the present invention and that the present invention be limited only by the hereinafter appended claims. 

We claim:
 1. A test kit for determining the presence of a hydroxy substituted aromatic compound which is suspected to be in a solution which comprises:(a) a titanium film formed from a reaction of a titanium alkoxide and an aliphatic carboxylic acid which changes light absorbance in the presence of the hydroxy substituted aromatic compound in the solution wherein the film is used for determination of a reaction of the hydroxy aromatic substituted compound after contact with a solution to be tested for the hydroxy substituted aromatic compound; (b) a sealed light transparent spectrophotometric container having a transparent element on which is deposited the film, which container is openable for inserting the solution to be tested, wherein the container is free of any hydroxy substituted aromatic compound; and (c) an absorbance detecting spectrophotometer means using visible to ultraviolet light adapted for use under field conditions for detecting the reaction of the hydroxy aromatic compound from the solution with the film because of a change of light absorbance of the titanium film.
 2. The test kit of claim 1 wherein the container is filled with an aqueous solution which is free of the hydroxy substituted aromatic compound.
 3. The test kit of claim 1 wherein the titanium alkoxide contains between 3 and 32 carbon atoms.
 4. The test kit of claim 3 wherein the titanium alkoxide is titanium isopropoxide.
 5. The test kit of claim 3 wherein the aliphatic carboxylic acid is an alkyl carboxylic acid containing between about 2 and 22 carbon atoms.
 6. The test kit of claim 3 wherein the titanium alkoxide is titanium isopropoxide and the aliphatic carboxylic acid is valeric acid.
 7. A test kit for determining the presence of a hydroxy substituted aromatic compound which is suspected to be in a solution which comprises:(a) a titanium film formed from a reaction of a titanium alkoxide and an aliphatic carboxylic acid which changes light absorbance in the presence of the hydroxy substituted aromatic compound in the solution, wherein the film is deposited on a transparent element inside a light transparent container which is used for determination of a reaction of the hydroxy aromatic substituted compound after contact with a solution to be tested for the hydroxy substituted aromatic compound; and (b) an absorbance detecting spectrophotometer means using visible to ultraviolet light adapted for use under field conditions for detecting the reaction of the hydroxy aromatic compound from the solution with the film because of a change of light absorbance of the titanium film. 